Cleaned the weld chamfers free from rust preventive coating. Welded erection irons (20 Nos) on both sides of the joint & pulled the sections together by draw bolt. Adjusting irons are welded in between the erection irons where shell overlap was found. Checked the alignment of the shell with the Piano wire arrangement. A gap of 3mm maintained in between the shell joint. Strong backs will be welded on one shell after initial alignment. Took polar readings on either side of the joint & both ends of the ShellsPlotted polar diagrams and checked the eccentricity. Tolerances: Eccentricity (radial runout ) must not exceed +/- 1. 0 mm of the inlet & outlet rings +/- 1. 5mm of the erection welds. +/-

1. 4mm of kiln section in the live ring. The axial untruth of live ring must not exceed +/- 1mm After completion of the alignment, weld the strong backs to the other side. Welding of Joint: Clean the joint surface. Preheat the joint area of the shell ( 1m lg ) to 150 deg Welding electrodes are to be preheated Complete the root run on the outer surface of the joint side with 2. 5mm electrode. Next with 4mm electrode & then 5mm & 6 mm electrodes. Gouge & remove the root run weld from the inner surface of the joint, check with Dye penetrant for any cracks and start the root run inside.  Complete the inside welding. Check the joint by Ultrasonic testing. Importance of Pre-heating: Preheating slows the cooling rate in the weld area. This may be necessary to avoid cracking of the weld metal or heat affected zone.

Hydrogen contributes to delayed weld and /or heat affected zone cracking, hence it is important to keep the weld joint free of oil, rust, paint, and moisture as they are sources of hydrogen. Electrodes used ( 1-2 joint) : FLS 9721 : E 7018 (3. 15mm ) Bottom runs FLS 9721 : E 7018 (4. 00mm) FLS 9721 : E 7018 (5mm) FLS 9732 : E 6027 for Cover Run E 7018 E 6027 Yield stress : 410-480360-410 N/sq. mm Tensile strength :510-590 440-490 N/sq. mm Elongation : 28% 27 Impact (Charpy V) +20deg c – approx. 14090 Electrodes used (other joints) : FLS 9727 : E 9018 (3. 15mm ) FLS 9727 : E 9018 (4. 00mm) FLS 9727 : E 9018 (5mm)FLS 9727: E 9018 ( 6mm) E 9018: Yield stress : 490-590 N/sq. mm Tensile strength : 640-740 N/sq. mm Elongation : 25% Impact (Charpy V) +20deg c – approx. 180

Order custom essay Hydrogen with free plagiarism report

GET ORIGINAL PAPER

This essay was written by a fellow student. You can use it as an example when writing your own essay or use it as a source, but you need cite it.

Get professional help and free up your time for more important courses

Starting from 3 hours delivery 450+ experts on 30 subjects
get essay help 124  experts online

Did you know that we have over 70,000 essays on 3,000 topics in our database?

Cite this page

Explore how the human body functions as one unit in harmony in order to life

Hydrogen. (2018, May 28). Retrieved from https://phdessay.com/hydrogen/

We use cookies to give you the best experience possible. By continuing we’ll assume you’re on board with our cookie policy

Save time and let our verified experts help you.

Hire writer